Comparative Properties for Aggressive Cooling Water Candidates
| Property | SEA-CURE® | Ti Grade 2 | 90-10 Cu/Ni | AL6XN® |
| Ultimate Strength* | 586 MPa | 345 MPa | 276 MPa | 689 MPa |
| Yield Strength* | 478 MPa | 276 MPa | 103 MPa | 310 MPa |
| Elongation* | 20% | 20% | 25% | 30% |
| Rockwell Hardness** | Rc 25 | Rb 92 | Rb 20 | Rb 100 |
| Modulus of Elasticity | 2.17 x 10^5 | 1.06 x 10^5*** | 1.24 x 10^5 | 1.94 x 10^5 |
| Density (kg/m^3) | 7.695 | 4.429 | 8.858 | 8.027 |
| Thermal Expansion (mm/mm-°C) |
9.68 | 9.4 | 17.1 | 15.7 |
| Thermal Conductivity (watts/m-°K) |
17.1 | 21.6 | 45.0 | 13.7 |
| Fatigue Endurance | 241 MPa | 110 MPa | 172 MPa | 227 MPa |
* Minimum ASTM Value
** Maximum ASTM Value
*** Average of Longitudinal and Transverse
More SEA-CURE® information is available at www.seacuresolutions.com.